DENISTAT Y 00U 03
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Vamp Tech |
| Trademark: | DENISTAT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3SFUb7_DENISTAT-Y-00U-03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66 unfilled, surface resistivity 10^3 ohm. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 120 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 6.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 50 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 245 | °C | ASTM D1525 1 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 100 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP VLF 80111 CC | RTP Company | PP, Unspecified | RTP |
| Texin® STX | Covestro - PUR | PUR, Unspecified | Texin® |
| EMOPLEN® CP MTF 10 FR V0 | EMAS Plastik San.Tic.AS. | PP Copolymer | EMOPLEN® |
| Sumiliteresin® PR-1305 I | SBHPP | Phenolic | Sumiliteresin® |
| LNP™ THERMOCOMP™ DC0049XF compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |