TAROMID B 280 G6 Y0
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3Qyrvp_TAROMID-B-280-G6-Y0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAROMID B 280 G6 Y0 is a Polyamide 6 (Nylon 6) product filled with 30% glass fiber. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 23°C, 3.20 mm | 0.40 to 0.70 | % | |
| Flow : 23°C, 3.20 mm | 0.25 to 0.35 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.5 | % | |
| Saturation, 23°C | 7.0 | % | |
| Granule Humidity 1 | < 0.10 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 8300 | MPa | ISO 178 |
| Flexural Stress 3 | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 90 | J/m | ASTM D256 |
| Notched Izod Impact (Area) (23°C) | 7.50 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed) | 215 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 220 | °C | ISO 306/B50 |
| Ball Pressure Test (170°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 222 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1.0 mm/min |
| 3 . | 1.0 mm/min |
| 4 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-1336B | Teknor Apex Company | TPE | Telcar® |
| DINALON® B1S25 C10-4172 | Grupo Repol | Nylon 6 | DINALON® |
| Globalene® TPV 1075A BK | Lee Chang Yung Chemical Industry Corp. | TPV | Globalene® |
| KEBATER® PBT BM330 | BARLOG plastics GmbH | PBT | KEBATER® |
| Silastic® Q7-4535 | Dow Corning Corporation | Silicone | Silastic® |