PEEK-OPTIMA® Granular
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Invibio Inc. |
| Trademark: | PEEK-OPTIMA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3Qpwyt_PEEK-OPTIMA-Granular.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PEEK-OPTIMA® polymer from Invibio® is a high performance biomaterial providing advanced solutions for implant manufacturers. Formulated to meet the most exacting in-vivo criteria, PEEK-OPTIMA is biocompatible, safe and stable. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.00 mm) | 1.2 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 99 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 100 | MPa | ISO 527-2/1B/50 |
| Tensile Strain (Break) | 20 | % | ISO 527-2/1B/50 |
| Flexural Modulus | 4000 | MPa | ISO 178 |
| Flexural Stress | 170 | MPa | ISO 178 |
| Compressive Strength | 118 | MPa | ASTM D695 |
| Shear Modulus | 1300 | MPa | ASTM D732 |
| Shear Strength | 53.1 | MPa | ASTM D732 |
| Poisson's Ratio | 0.40 | ASTM E132 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 63 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 340 | °C | DSC |
| CLTE - Flow | ASTM D696 | ||
| -- 1 | 4.7E-5 | cm/cm/°C | ASTM D696 |
| -- 2 | 1.1E-4 | cm/cm/°C | ASTM D696 |
| RTI Elec | 260 | °C | UL 746 |
| RTI Imp | 260 | °C | UL 746 |
| RTI | 260 | °C | UL 746 |
| Additional Information |
|---|
| Heat Distortion Temperature, ISO 75: 306°F |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Max Regrind | 0 | % | |
| Rear Temperature | 350 - 355 | °C | |
| Middle Temperature | 355 - 365 | °C | |
| Front Temperature | 360 - 370 | °C | |
| Nozzle Temperature | 365 - 375 | °C | |
| Mold Temperature | 160 - 200 | °C | |
| Injection Pressure | 7.00 - 14.0 | MPa | |
| Holding Pressure | 4.00 - 10.0 | MPa | |
| Back Pressure | 0.200 - 5.00 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Clamp Tonnage | 5.0 - 8.0 | kN/cm² | |
| Screw L/D Ratio | 18.0:1.0 - 24.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Note Message | |
|---|---|
| 1 . | Below Tg |
| 2 . | Above Tg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fiberfil® PP-60/CC/40 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| DOKI® PS 457 | DIOKI d.d. | PS (HIPS) | DOKI® |
| Hylon® N1033MDHL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| LNP™ LUBRICOMP™ CG006 compound | SABIC Innovative Plastics Europe | PS (HIPS) | LNP™ LUBRICOMP™ |
| Sylvin 7833-90 Grey 9193 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |