Generic PC - Glass Fiber
| Category: | PC , Polycarbonate |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3QUF7G_Generic-PC---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PC - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.24 - 1.52 | g/cm³ | ASTM D792 |
| 23°C | 1.24 - 1.44 | g/cm³ | ISO 1183 |
| -- | 1.25 - 1.65 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.64 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | |||
| 300°C/1.2 kg | 3.8 - 19 | g/10 min | ASTM D1238 |
| 300°C/1.2 kg | 2.1 - 15 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 2.79 - 14.2 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 4.0E-3 - 0.50 | % | ASTM D955 |
| Transverse flow : 23°C | 0.20 - 0.73 | % | ASTM D955 |
| 23°C | 0.18 - 0.50 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.059 - 0.22 | % | ASTM D570 |
| 23°C, 24 hr | 0.076 - 0.40 | % | ISO 62 |
| Saturated, 23°C | 0.070 - 0.30 | % | ASTM D570 |
| Saturated, 23°C | 0.068 - 0.31 | % | ISO 62 |
| Equilibrium, 23°C | 0.24 - 0.32 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.068 - 0.22 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 84 - 124 | ASTM D785 | |
| 23°C | 65 - 121 | ISO 2039-2 | |
| Ball Indentation Hardness | 115 - 151 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2610 - 9730 | MPa | ASTM D638 |
| 23°C | 2970 - 9600 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 49.1 - 127 | MPa | ASTM D638 |
| Yield, 23°C | 52.7 - 121 | MPa | ISO 527-2 |
| Fracture, 23°C | 33.8 - 143 | MPa | ASTM D638 |
| Fracture, 23°C | 43.9 - 131 | MPa | ISO 527-2 |
| 23°C | 54.4 - 147 | MPa | ASTM D638 |
| 23°C | 45.0 - 100 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 2.1 - 5.0 | % | ASTM D638 |
| Yield, 23°C | 1.9 - 5.1 | % | ISO 527-2 |
| Fracture, 23°C | 0.0 - 7.5 | % | ASTM D638 |
| Fracture, 23°C | 1.0 - 5.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2980 - 8550 | MPa | ASTM D790 |
| 23°C | 2790 - 8730 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 82.3 - 221 | MPa | ASTM D790 |
| 23°C | 89.5 - 182 | MPa | ISO 178 |
| Yield, 23°C | 88.4 - 183 | MPa | ASTM D790 |
| Fracture, 23°C | 109 - 190 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 69.8 - 152 | MPa | ASTM D695 |
| Coefficient of Friction | 0.18 - 0.58 | ASTM D1894 | |
| Taber Abrasion Resistance (23°C) | 11.0 - 17.3 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.7 - 25 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 26 - 71 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 64 - 160 | J/m | ASTM D256 |
| 23°C | 7.0 - 25 | kJ/m² | ISO 180 |
| Notched Izod Impact (23°C) | 10.0 - 10.1 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact | |||
| 23°C | 93 - 2100 | J/m | ASTM D256 |
| 23°C | 34 - 75 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 9.15 - 61.0 | J | ASTM D3763 |
| 23°C | 2.15 - 9.29 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force (23°C) | 885 - 4030 | N | ISO 6603-2 |
| Dart Drop Impact (23°C) | 0.452 - 102 | J | ASTM D3029 |
| Tensile Impact Strength (23°C) | 53.3 - 158 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 136 - 153 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 139 - 149 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 144 - 149 | °C | ASTM D648 |
| 0.45 MPa, annealed | 143 - 148 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 133 - 152 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 131 - 146 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 135 - 143 | °C | ASTM D648 |
| 1.8 MPa, annealed | 131 - 144 | °C | ISO 75-2/A |
| Continuous Use Temperature | 129 - 133 | °C | ASTM D794 |
| Glass Transition Temperature | 148 | °C | DSC |
| Vicat Softening Temperature | |||
| -- | 143 - 169 | °C | ASTM D1525 |
| -- | 142 - 154 | °C | ISO 306 |
| Ball Indentation Temperature | 125 - 140 | °C | IEC 60598-1 |
| Linear thermal expansion coefficient | |||
| Flow | 1.9E-5 - 4.6E-5 | cm/cm/°C | ASTM D696 |
| Flow | 2.1E-5 - 5.0E-5 | cm/cm/°C | ASTM E831 |
| Flow | 1.9E-5 - 5.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.0E-6 - 7.5E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 5.2E-5 - 7.2E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 6.0E-5 - 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 1050 - 1250 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | |||
| 23°C | 0.13 - 0.35 | W/m/K | ASTM C177 |
| 23°C | 0.21 - 0.30 | W/m/K | ISO 8302 |
| RTI Elec | 79.1 - 130 | °C | UL 746 |
| RTI Imp | 75.0 - 130 | °C | UL 746 |
| RTI | 75.0 - 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 5.0 - 7.2E+15 | ohms | ASTM D257 |
| -- | 1.0E+4 - 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 0.0 - 2.5E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+13 - 2.5E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 16 - 30 | kV/mm | ASTM D149 |
| 23°C | 15 - 37 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.00 - 3.54 | ASTM D150 | |
| 23°C | 2.95 - 5.13 | IEC 60250 | |
| 23°C | 3.21 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 8.0E-4 - 0.010 | ASTM D150 | |
| 23°C | 8.0E-4 - 9.4E-3 | IEC 60250 | |
| Arc Resistance | 100 - 120 | sec | ASTM D495 |
| Comparative Tracking Index | 171 - 175 | V | IEC 60112 |
| Insulation Resistance (23°C) | 1.0E+4 - 1.0E+12 | ohms | IEC 60167 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 957 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 824 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | |||
| -- | 30 - 40 | % | ASTM D2863 |
| -- | 35 - 38 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 119 - 122 | °C | |
| Drying Time | 2.9 - 4.1 | hr | |
| Drying Time, Maximum | 27 | hr | |
| Dew Point | -28.9 - -28.6 | °C | |
| Suggested Max Moisture | 0.020 - 0.024 | % | |
| Suggested Shot Size | 50 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 276 - 316 | °C | |
| Middle Temperature | 289 - 316 | °C | |
| Front Temperature | 288 - 329 | °C | |
| Nozzle Temperature | 269 - 321 | °C | |
| Processing (Melt) Temp | 288 - 323 | °C | |
| Mold Temperature | 79.0 - 103 | °C | |
| Injection Pressure | 84.6 - 123 | MPa | |
| Holding Pressure | 6.89 - 90.0 | MPa | |
| Back Pressure | 0.150 - 1.98 | MPa | |
| Screw Speed | 45 - 76 | rpm | |
| Cushion | 4.76 - 9.53 | mm | |
| Vent Depth | 0.051 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PC - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCUDIA® LDPE 2203F | REPSOL | LDPE | ALCUDIA® LDPE |
| CYCOLAC™ INP362 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| Geon™ Vinyl Packaging 161J-1-3V/2188GC-3V | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Packaging |
| Karina IVORY PVC COMPOUND -E 700-35/1-EX | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MARPOL® HDB 506 | Marco Polo International, Inc. | HDPE, MMW | MARPOL® |