MBA PP 2123
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | MBA Polymers |
| Trademark: | MBA PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3PyKvr_MBA-PP-2123.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A post-consumer recycled polypropylene copolymer for general use. Available in standard black (reference 90/04). |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | Internal Method |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 20.0 | MPa | ISO 527-2/50 |
| Flexural Modulus (23°C) | 1000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 6.0 | kJ/m² | |
| 23°C | 10 | kJ/m² |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Melt Temperature | 180 to 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Qenos PP PPW 1780 | Qenos Pty Ltd | PP Homopolymer | Qenos PP |
| Starex TX-0530T | SAMSUNG SDI CO., LTD. | MABS | Starex |
| VENYL UG207 - 8071 | AD majoris | Nylon 66 | VENYL |
| VECTRA® E845i LDS | Celanese Corporation | LCP | VECTRA® |
| CALP 3511G | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |