Centrex® 485CS
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Centrex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3OX3k9_Centrex-485CS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Centrex®485CS is an acrylonitrile-styrene-acrylate (ASA) product,. It can be processed by co-extrusion, extrusion or thermoforming and is available in North America. Centrex®The application areas of 485CS include the automotive industry and outdoor applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 5.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 69 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1450 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 26.5 | MPa | ASTM D638 |
| Flexural Modulus - Tangent 3 | 1380 | MPa | ASTM D790 |
| Flexural Strength 4 | 38.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 43 | J/m | ASTM D256 |
| -18°C, 3.18 mm | 64 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 130 | J/m | ASTM D256 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 6.00 | J | ASTM D3763 |
| -18°C, Total Energy | 16.0 | J | ASTM D3763 |
| 23°C, Total Energy | 24.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 68.3 | °C | ASTM D648 |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 |
| CLTE - Flow | 9.4E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 60° 5 | 10 | ASTM D523 | |
| 60° 6 | 20 | ASTM D523 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 93.3 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.030 | % | |
| Melt Temperature | 204 - 243 | °C | |
| Die Temperature | 210 - 241 | °C |
| Extrusion instructions |
|---|
| Recommended Regrind: up to 40%Polish roll Top: Down stack 200°F, Up stack 200°FPolish roll Middle: Down stack 165°F, Up stack 190°FPolish roll Bottom: Down stack 200°F, Up stack 180°F |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | 5.1 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Formed |
| 6 . | Sheet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| mPact™ D139EK | Chevron Phillips Chemical Company LLC | mLLDPE | mPact™ |
| Niche PA66GI14BK | Niche Polymer, LLC | Nylon 66 | Niche |
| Axiall PVC 9202J | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Infino WP-1098 | SAMSUNG SDI CO., LTD. | PC+ABS | Infino |
| Crastin® SK605LM BK591 | DuPont Performance Polymers | PBT | Crastin® |