UmaPET WH
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Ester Industries Ltd. |
| Trademark: | UmaPET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3O1ZAf_UmaPET-WH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
KEY FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | ASTM D1204 | ||
| Flow : 150°C, 30 min, 0.0300 mm | 2.5 | % | |
| Flow : 150°C, 30 min, 0.0360 mm | 2.5 | % | |
| Flow : 150°C, 30 min, 0.0500 mm | 2.0 | % | |
| Flow : 150°C, 30 min, 0.0750 mm | 2.0 | % | |
| Across Flow : 150°C, 30 min, 0.0300 mm | 0.60 | % | |
| Across Flow : 150°C, 30 min, 0.0360 mm | 0.60 | % | |
| Across Flow : 150°C, 30 min, 0.0500 mm | 0.60 | % | |
| Across Flow : 150°C, 30 min, 0.0750 mm | 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic 1 | 0.40 | ||
| vs. Itself - Dynamic 2 | 0.40 | ||
| vs. Itself - Dynamic 3 | 0.40 | ||
| vs. Itself - Dynamic 4 | 0.40 | ||
| vs. Itself - Static 5 | 0.50 | ||
| vs. Itself - Static 6 | 0.50 | ||
| vs. Itself - Static 7 | 0.50 | ||
| vs. Itself - Static 8 | 0.50 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 36 50 75 | µm | |
| Film Thickness - Recommended / Available | 30, 36, 50, 75 µm | ||
| Tensile Strength | ASTM D882 | ||
| MD : Break, 30 µm | 167 | MPa | |
| MD : Break, 36 µm | 157 | MPa | |
| MD : Break, 50 µm | 157 | MPa | |
| MD : Break, 75 µm | 147 | MPa | |
| TD : Break, 30 µm | 177 | MPa | |
| TD : Break, 36 µm | 167 | MPa | |
| TD : Break, 50 µm | 167 | MPa | |
| TD : Break, 75 µm | 157 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm | 120 | % | |
| MD : Break, 36 µm | 120 | % | |
| MD : Break, 50 µm | 120 | % | |
| MD : Break, 75 µm | 120 | % | |
| TD : Break, 30 µm | 80 | % | |
| TD : Break, 36 µm | 80 | % | |
| TD : Break, 50 µm | 80 | % | |
| TD : Break, 75 µm | 80 | % | |
| Yield | Internal Method | ||
| 5.00 nm | 14.1 | m²/kg | |
| 30.0 µm | 23.8 | m²/kg | |
| 36.0 µm | 19.8 | m²/kg | |
| 75.0 µm | 9.40 | m²/kg |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Wetting Tension | ASTM D2578 | ||
| 30.0 µm | 44 | dyne/cm | |
| 36.0 µm | 44 | dyne/cm | |
| 50.0 µm | 44 | dyne/cm | |
| 75.0 µm | 44 | dyne/cm |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Opacity | Internal Method | ||
| -- 9 | 88 | % | |
| -- 10 | 90 | % | |
| -- 11 | 90 | % | |
| -- 12 | 92 | % | |
| Haze | ASTM D1003 | ||
| 30.0 µm | 98 | % | |
| 36.0 µm | 98 | % | |
| 50.0 µm | 98 | % | |
| 75.0 µm | 98 | % |
| Note Message | |
|---|---|
| 1 . | 50 µm |
| 2 . | 36 µm |
| 3 . | 75 µm |
| 4 . | 30 µm |
| 5 . | 75 µm |
| 6 . | 50 µm |
| 7 . | 36 µm |
| 8 . | 30 µm |
| 9 . | 30 µm |
| 10 . | 50 µm |
| 11 . | 36 µm |
| 12 . | 75 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultraform® W 2320 003 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Adsyl 6 C 30 F | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |
| Edgetek™ TR2-10GF/000 NATURAL | PolyOne Corporation | Copolyester | Edgetek™ |
| Ekatal® H 3 | Sattler KunststoffWerk GmbH | Acetal (POM) Copolymer | Ekatal® |
| K-Bin Rigid PVC KBD-3045 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |