Hylex® P1025G20HB
| Category: | PC , Polycarbonate |
| Manufacturer: | Ravago Manufacturing Americas, LLC |
| Trademark: | Hylex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3NVwB9_Hylex-P1025G20HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate, High Flow, 20% Glass Filled |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 to 0.40 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 92 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 93.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 5170 | MPa | ISO 178 |
| Flexural Stress | 124 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 7.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 134 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 129 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SPESIN® KP212G15V0BLS | Kolon Plastics, Inc. | PBT | SPESIN® |
| TOTAL Polyethylene XSene® HDPE XRC20 Orange | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| Garaflex™ E 4362-A1 NAT LCF | AlphaGary | TPE | Garaflex™ E |
| Geon™ Vinyl Rigid Extrusion L6181 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Hostacom PPN 4160 | LyondellBasell Industries | PP Homopolymer | Hostacom |