RTP 204 A FR UV
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3NRGAV_RTP-204-A-FR-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber - Flame Retardant - UV Stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.63 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 - 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.3 | % | ASTM D570 |
| Moisture Content | 0.20 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 25 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10300 | MPa | ASTM D638 |
| Tensile Strength | 124 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.0 - 3.0 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 85 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 690 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 193 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Dew Point | -17.8 | °C | |
| Processing (Melt) Temp | 243 - 279 | °C | |
| Mold Temperature | 54.4 - 93.3 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Beamset 101 | Arakawa Chemical Industries, Ltd. | Epoxy | Beamset |
| ISPLEN® PP 089 Y1E | REPSOL | PP Homopolymer | ISPLEN® |
| Jiangsu Sinarise ZM70 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| POLLITE 1001C | POLYROCKS CHEMICAL CO., LTD | PC | POLLITE |
| ALTECH® PA66 ECO 1000/618 IM | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |