FERREX® GPP30RA03HB
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ferro Corporation |
| Trademark: | FERREX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3NMdGo_FERREX-GPP30RA03HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FERREX®GPP30RA03HB is a polypropylene material, and its filler is 30% calcium carbonate filler. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. FERREX®The main characteristics of the GPP30RA03HB are: high gloss. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.5 | % | ASTM D955 |
| Transverse flow | 1.9 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 21.4 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 150 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : 23°C | 1700 | MPa | ASTM D790 |
| Tangent : 23°C | 2060 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 36.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 880 | J/m | ASTM D256 |
| Dart Drop Impact | 15.3 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 104 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 54.4 | °C | ASTM D648 |
| Additional Information |
|---|
| Filler Content, ASTM D2584: 32% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2770 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Viton® E-45 | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| TRILOY® 120 | Samyang Corporation | PC+PBT | TRILOY® |
| Hostacom CR 1171 G1 | LyondellBasell Industries | PP Impact Copolymer | Hostacom |
| OnForce™ LFT NN-40LGF/000 HS UV Black | PolyOne Corporation | Nylon 66 | OnForce™ LFT |