LNP™ THERMOCOMP™ RX04515H compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3NLSRP_LNP-THERMOCOMP-RX04515H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RX04515H is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Healthcare. Also known as: LNP* THERMOCOMP* Compound PDX-R-04515 EES HC Product reorder name: RX04515H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.40 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 30800 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 278 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.6 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 23700 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 100 mm Span) | 413 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 970 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 255 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax SV956 | LyondellBasell Industries | PP Impact Copolymer | Pro-fax |
| RTP VLF 82209 | RTP Company | PEEK | RTP |
| SABIC® LDPE 2102N0W | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| VICTREX® PEEK 450GL30 BLACK | Victrex plc | PEEK | VICTREX® PEEK |
| Sylvin 9077-90 Blue 8476 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |