VITAMIDE® AR36BK9004
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3NL18C_VITAMIDE-AR36BK9004.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® AR36BK9004 is a Polyamide 66 (Nylon 66) product filled with 30% glass fiber. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 0.80 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 150 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 200 | MPa | ISO 178 |
| Break | 200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 40 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | 7.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 240 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 235 | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 260 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 28 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature 1 | 650 | °C | IEC 60695-2-13 |
| Oxygen Index | 23 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 30 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 TFE 10 SI | RTP Company | Nylon 66 | RTP |
| SILVER® SA-5302 | Guangdong Silver Age Sci & Tech. Co., Ltd | Polyolefin, Unspecified | SILVER® |
| 3M™ Dyneon™ PTFE Compound TFX 4262 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Eltex® P HEY500 | INEOS Olefins & Polymers Europe | PP+PE | Eltex® P |
| Elvacite® 2013 | Lucite International Inc. | Acrylic (PMMA) | Elvacite® |