OP - Acetal C-Acetal 20PTFE
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Oxford Polymers |
| Trademark: | OP - Acetal |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3Ldp6Q_OP---Acetal-C-Acetal-20PTFE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OP - Acetal C-Acetal 20PTFE is an Acetal (POM) Copolymer material filled with 20% ptfe fiber. It is available in North America for injection molding. Important attributes of OP - Acetal C-Acetal 20PTFE are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 to 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 41.4 | MPa | |
| Break | 41.4 | MPa | |
| Tensile Elongation (Break) | 13 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 62.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4°C) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 110 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 98.9 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | V-0 | ||
| 3.18 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 177 to 199 | °C | |
| Middle Temperature | 182 to 204 | °C | |
| Front Temperature | 188 to 210 | °C | |
| Processing (Melt) Temp | 182 to 218 | °C | |
| Mold Temperature | 79.4 to 107 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Smoothblend® PC-1301 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC | Smoothblend® |
| Ultramid® B3EG10 | BASF Corporation | Nylon 6 | Ultramid® |
| 3M™ Dyneon™ PTFE Compound TF 4705 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Lotrène® LLDPE Q1018N | QATOFIN Company Limited | LLDPE | Lotrène® LLDPE |
| Lupoy® 1201-10 | LG Chem Ltd. | PC | Lupoy® |