PRL PPX-SF1
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3LTgO6_PRL-PPX-SF1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PPX-SF1 is a Polyphenylene Ether + PS (PPE+PS) product. It can be processed by structural foam molding and is available in North America. Typical application: Foam. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/11.6 kg) | 25 to 50 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18 mm | 0.60 to 0.90 | % | |
| Across Flow : 3.18 mm | 0.60 to 0.90 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 63.4 | MPa | |
| Break, 3.18 mm | 62.1 | MPa | |
| Flexural Modulus (3.18 mm) | 3170 | MPa | ASTM D790 |
| Flexural Strength (Break, 3.18 mm) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 110 | J/m | ASTM D256 |
| Gardner Impact (3.18 mm) | 16.9 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 104 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 98.9 | °C | |
| RTI Elec | UL 746 | ||
| 3.00 mm | 65.0 | °C | |
| 3.80 mm | 65.0 | °C | |
| RTI Imp | UL 746 | ||
| 3.00 mm | 65.0 | °C | |
| 3.80 mm | 65.0 | °C | |
| RTI Str | UL 746 | ||
| 3.00 mm | 65.0 | °C | |
| 3.80 mm | 65.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm | V-0 | ||
| 3.80 mm | V-0 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 232 to 260 | °C | |
| Middle Temperature | 271 to 304 | °C | |
| Front Temperature | 271 to 304 | °C | |
| Processing (Melt) Temp | 260 to 288 | °C | |
| Mold Temperature | 37.8 to 82.2 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA S511 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| Vital-Line SHE7000 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Ultramid® B3GM35 BKQ642 23220 | BASF Corporation | Nylon 6 | Ultramid® |
| CarmelStat™ CS 6015 | Carmel Olefins Ltd. | PP, Unspecified | CarmelStat™ |
| Haysite Plastics HCR-196 | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |