NORYL GTX™ GTX918WR resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3LRAXp_NORYL-GTX-GTX918WR-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High flow PPE+PA for under-the-hood and electrical applications. With mold release |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 45 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/1.2 kg) | 5.30 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 1.3 - 1.6 | % | Internal method |
| Transverse flow : 3.20mm | 1.0 - 1.3 | % | Internal method |
| Water Absorption (Saturation, 23°C) | 4.2 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 818 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 2 | 62.1 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 57.9 | MPa | ASTM D638 |
| Fracture | 55.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 11 | % | ASTM D638 |
| Yield | 4.5 | % | ISO 527-2/50 |
| Fracture 5 | 53 | % | ASTM D638 |
| Fracture | 30 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2360 | MPa | ASTM D790 |
| -- 7 | 2200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 85.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 98.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 200 | J/m | ASTM D256 |
| -30°C 10 | 10 | kJ/m² | ISO 180/1A |
| 23°C 11 | 20 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 40.7 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 189 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span 12 | 185 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.20mm | 149 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 242 | °C | ASTM D1525 13 |
| -- | 245 | °C | ISO 306/A50 |
| -- | 190 | °C | ISO 306/B50 |
| -- | 195 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 6.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 60°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 60°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.25 | W/m/K | ASTM C177 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 - 107 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Suggested Shot Size | 30 - 50 | % | |
| Rear Temperature | 254 - 293 | °C | |
| Middle Temperature | 260 - 293 | °C | |
| Front Temperature | 266 - 293 | °C | |
| Nozzle Temperature | 271 - 293 | °C | |
| Processing (Melt) Temp | 271 - 293 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Back Pressure | 0.345 - 1.38 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.013 - 0.038 | mm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.02 % |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 120*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starflam BFR200Y | Eurostar Engineering Plastics | Nylon 6 | Starflam |
| Geon™ Vinyl Flexible R881C | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| POLIMAXX 2311NCXTA4 | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |
| Hifax TRC 277P G14008 | LyondellBasell Industries | PP Copolymer | Hifax |
| RONFALIN® ABS 1326 | A. Schulman Europe | ABS | RONFALIN® |