RTP VLF 82307 A
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3KBZZi_RTP-VLF-82307-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Long Glass Fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 - 0.20 | % | ASTM D955 |
| Moisture Content | 0.010 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ASTM D638 |
| Tensile Strength | 228 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.5 - 3.5 | % | ASTM D638 |
| Flexural Modulus | 10000 | MPa | ASTM D790 |
| Flexural Strength | 324 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 480 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 1600 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 93.3 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 107 | °C | |
| Drying Time | 6.0 | hr | |
| Dew Point | -40.0 | °C | |
| Processing (Melt) Temp | 221 - 243 | °C | |
| Mold Temperature | 51.7 - 93.3 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. To maximize fiber length, the following injection barrel, screw, and tip designs should be followed. L/D ratio 16/1 - 22/1, Compression ratio 2:1, Flight depth 0.200 in (5 mm) minimum, in feed section, Screw diameter 0.65 - 0Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ MTX90 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| RTP 800 GB 30 DEL | RTP Company | Acetal (POM) Homopolymer | RTP |
| Resiprene® 1050 | Resirene, S.A. de C.V. | TPE | Resiprene® |
| Hifax SP 1079/94 | LyondellBasell Industries | PP Copolymer | Hifax |
| Sylvin 8200-85 White 1524 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |