UNIVAL™ DMDG-6240 NT 7
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | UNIVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3Hb3Uu_UNIVAL-DMDG-6240-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UNIVAL™ DMDG-6240 NT 7 is a multipurpose polymer designed for high speed production of blow molded containers used to package household industrial chemicals, such as laundry detergent, health and medicinal aids as well as agricultural and food products. The product is specifically designed to provide excellent processing in all extrusion blow molding equipment. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.946 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.40 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 43 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 400 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 23.8 | MPa | ASTM D638 |
| Fracture | 16.5 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 11 | % | ASTM D638 |
| Fracture | 770 | % | ASTM D638 |
| Flexural Modulus | ASTM D790B | ||
| 1% secant | 1020 | MPa | ASTM D790B |
| 2% secant | 814 | MPa | ASTM D790B |
| Tangent | 1150 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 151 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 62.8 | °C | ASTM D648 |
| Brittleness Temperature | < -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 121 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 126 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 108 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行基板模制和测试。 |
| Note Message | |
|---|---|
| 1 . | Type s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SIM5029R | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Sylvin 8463-60 Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |
| NEFTEKHIM PE 6749F (486H6) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| GECET™ F-300 | Fagerdala USA Inc. | PS (EPS) | GECET™ |
| Huafon HF-1275AP | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |