Hifax TRC 135X/4 BLACK
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3HXvq4_Hifax-TRC-135X-4-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP/EPR-Blend, 20% mineralfilled, impact modified, with ultra low shrinkage and high flowability for painted exterior applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 23°C, 4 hr | 0.55 | % | |
| Flow : 23°C, 4 hr | 0.35 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1400 | MPa | ISO 527-2/50 |
| Tensile Stress (Yield, 23°C) | 17.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 550 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 1500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/eA | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 72 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 95.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 110 | °C | ISO 306/A50 |
| CLTE - Flow | 4.3E-5 | cm/cm/°C | DIN 53752 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC6PAZ (Series: AD/PA) | KRAIBURG TPE | TPE | THERMOLAST® K |
| TEREZ PA 6 7510 GF 10 MF 30 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Evoprene™ 076 | AlphaGary | SBS | Evoprene™ |
| Lucet® FW-700S | LG Chem Ltd. | Acetal (POM) Copolymer | Lucet® |
| OTECH ALLOY OE7828 - Calendering | OTECH Corporation | TP, Unspecified | OTECH ALLOY |