China PPS hMR60/1
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Sichuan Deyang Chemical Co., Ltd |
| Trademark: | China PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3HGuSc_China-PPS-hMR60-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPS-hMR60/1 is filled and reinforced PPS compound, which is filled with mineral and glass fiber based on the PPS resin. High flow. With a comparative low price, it shows high rigidity, creep resistance, low mold shrinkage, high-temperature resistance, inherent flame resistance, excellent electrical insulation properties, easy processing and good dimensional stability. Owing to its high performance and comparative low price, it is widely used in electronic/electric appliances, automobile, home appliances, and mechanical fields etc. And it's an excellent selection for small parts, connector, plugs and terminals with thin wall insets etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.81 | g/cm³ | Internal method |
| Molding Shrinkage | Internal method | ||
| Flow | 0.25 | % | Internal method |
| Transverse flow | 0.75 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness 1 | 110 | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 172 | MPa | Internal method |
| Tensile Elongation (Break) | 1.3 | % | Internal method |
| Flexural Modulus | 15400 | MPa | Internal method |
| Flexural Strength | 257 | MPa | Internal method |
| Compressive Strength | 140 | MPa | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 10 | kJ/m² | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | Internal method |
| Melting Temperature | 282 | °C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+14 | ohms | Internal method |
| Volume Resistivity | 2.0E+16 | ohms·cm | Internal method |
| Dielectric Strength | 15 | kV/mm | Internal method |
| Dielectric Constant (1 MHz) | 4.00 | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 300 - 320 | °C | |
| Front Temperature | 300 - 320 | °C | |
| Nozzle Temperature | 290 - 320 | °C | |
| Processing (Melt) Temp | 160 - 180 | °C | |
| Mold Temperature | 100 - 150 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Back Pressure | 0.100 - 1.00 | MPa | |
| Screw Speed | 40 - 100 | rpm |
| Injection instructions |
|---|
| Processing time: 4 to 16hr |
| Note Message | |
|---|---|
| 1 . | HR |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIKASUPER® LCP E6810F | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| Nypol® PA B2 G30 UV BRC0001 NT207 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| APEX® 94-A0098A-65 | Teknor Apex Company | PVC, Flexible | APEX® |
| Epoxies, Ect. 60-7108 | Epoxies, Etc. | Acrylic, Unspecified | Epoxies, Ect. |
| Plaslube® PA6/6 GF33 TS15 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |