SABIC® STAMAX 20YK270
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® STAMAX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3GzzxG_SABIC-STAMAX-20YK270.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® STAMAX 20YK270 is a 20% long glass fiber reinforced grade with improved impact and flow properties. The glass fibres are chemically coupled to the PP matrix, resulting in high stiffness and strength. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1B | ||
| 23°C, Injection Molded | 4450 | MPa | |
| 80°C, Injection Molded | 3250 | MPa | |
| 120°C, Injection Molded | 2850 | MPa | |
| Tensile Stress 1 | ISO 527-2 | ||
| 23°C, Injection Molded | 80.0 | MPa | |
| 80°C, Injection Molded | 54.0 | MPa | |
| 120°C, Injection Molded | 40.0 | MPa | |
| Tensile Strain (Break, 23°C, Injection Molded) | 2.4 | % | ISO 527-2/1B |
| Flexural Modulus | ISO 178 | ||
| 23°C, Injection Molded | 3900 | MPa | |
| 80°C, Injection Molded | 2850 | MPa | |
| Flexural Stress | ISO 178 | ||
| 23°C, Injection Molded | 108 | MPa | |
| 80°C, Injection Molded | 63.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Injection Molded | 18 | kJ/m² | |
| 23°C, Injection Molded | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C, Injection Molded | 56 | kJ/m² | |
| 23°C, Injection Molded | 49 | kJ/m² | |
| Falling Dart Impact - Total Energy 2(23°C) | 47.0 | J/cm | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 156 | °C | ISO 75-2/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 6.8E-5 | cm/cm/°C | |
| 23 to 80°C | 5.4E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Type 1B |
| 2 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M800U (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Copolymer | Sanren |
| TRIPET® LV2550GN30 | Samyang Corporation | PET | TRIPET® |
| UBESTA 3024 LU | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| Nypol® PA A3 G25 PRTA011 NR306 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Epoxies, Ect. 20-2121 | Epoxies, Etc. | PUR, Unspecified | Epoxies, Ect. |