Celstran® PP-GF30-05 natural
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3GuPD1_CelstranPPGF3005natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Heat stabilized polypropylene copolymer reinforced with 30 weight percent long glass fibers. The fibers are chemically coupled to the polypropylene matrix. The impact properties are enhanced. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. (-0501 = heat stabilized,) Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functionial/structural parts for automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 6300 | MPa | ISO 527-2/1A/1 |
| 80°C | 4400 | MPa | ISO 527-2/1A |
| Tensile Stress | |||
| Fracture | 110 | MPa | ISO 527-2/1A/5 |
| 80°C | 70.0 | MPa | ISO 527-2/1A |
| Tensile Strain | |||
| Fracture | 2.3 | % | ISO 527-2/1A/5 |
| Fracture, 80°C | 2.8 | % | ISO 527-2/1A |
| Flexural Modulus | ISO 178 | ||
| 23°C | 6500 | MPa | ISO 178 |
| 80°C | 4400 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 23°C | 160 | MPa | ISO 178 |
| 80°C | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 29 | kJ/m² | ISO 179/1eA |
| 23°C | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 80 | kJ/m² | ISO 179/1eU |
| 23°C | 70 | kJ/m² | ISO 179/1eU |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 68 | kJ/m² | ISO 180/1U |
| 23°C | 55 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy (-30°C) | 21.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 156 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 117 | °C | ISO 75-2/C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 - 100 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 240 - 250 | °C | |
| Front Temperature | 250 - 260 | °C | |
| Nozzle Temperature | 240 - 270 | °C | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 30 - 70 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Feed Temperature: 20 to 50°CZone 4 Temperature: 260 to 270°CManifold Temperature: 240 to 270°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santron IMS1000 SPARKLE | Bhansali Engineering Polymers Limited | SAN | Santron |
| Nylene® 451 | Custom Resins Group | Nylon 6 | Nylene® |
| CABELEC® CA4857 | Cabot Corporation | PS (GPPS) | CABELEC® |
| Elastron® G G103.A70.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Hostacom TRC 364N G82732 | LyondellBasell Industries | PP Copolymer | Hostacom |