NILSAN S MR K17V
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | NILSAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3GMKwH_NILSAN-S-MR-K17V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS 17% glass fibres reinforced, good dimensional stability, low shrinkage, good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.30 - 0.80 | % | Internal method |
| Flow direction | 0.10 - 0.30 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.10 | % | ISO 62 |
| Saturated, 23°C | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 78.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 5200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2(1.8 MPa, Unannealed) | 96.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 3 | 75.0 | °C | IEC 60216 |
| Vicat Softening Temperature | |||
| -- | 108 | °C | ISO 306/A50 |
| -- | 104 | °C | ISO 306/B50 |
| Ball Pressure Test (100°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow (-30 to 30°C) | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 550 | °C | IEC 60695-2-13 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 4(750°C) | 17 | % | ISO 3451 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Rate | Slow-Moderate |
| Injection instructions |
|---|
| Pre-heat Temperature: 70 to 80°CPre-heat Time: 3 hrs |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 120°C/hr |
| 3 . | 20,000 hr |
| 4 . | 1 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Small Boss SPVC8014 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | PVC, Unspecified | Small Boss |
| SUSTARIN® H | Röchling Sustaplast SE & Co. KG | Acetal (POM) Homopolymer | SUSTARIN® |
| Expandable PS RP33W | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| Flontech® FT-CARR15-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| TECHNYL® A 205F BLACK 651 | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |