TIPELIN® 7111S
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | MOL Petrochemicals Co. Ltd. |
| Trademark: | TIPELIN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3GFnHI_TIPELIN-7111S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bimodal HDPE for sheet extrusion and blow moulding TIPELIN 7111S is a high density bimodal polyethylene copolymer (with butene-1 as comonomer) intended for sheet extrusion and blow moulding of products with high stiffness, excellent environmental stress crack resistance, full notched creep behavior and improved long-term color stability. The grade contains antioxidants and acid scavengers. TIPELIN 7111S is recommended for the extrusion of sheets of industrial parts and consumer packaging as well, highly recommended in cases when better colour stability and lower yellowness value of the product is needed. TIPELIN 7111S is also recommended for non-pressure pipe extrusion and for blow moulding of jerry cans for the packaging even of aggressive industrial chemicals. TIPELIN 7111S is suitable for food contact, for manufacturing of toys. The product complies with Food Contact and Toy Safety Regulations. Receiving of certifications is in progress. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.949 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.12 | g/10 min | |
| 190°C/21.6 kg | 13 | g/10 min | |
| 190°C/5.0 kg | 0.50 | g/10 min | |
| Environmental Stress-Cracking Resistance (10% Igepal CO-630, F50) | > 10000 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (Injection Molded) | 1350 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 70 | µm | |
| Tensile Stress | ISO 527-3 | ||
| Yield, 70 µm, Blown Film | 25.0 | MPa | |
| Break, 70 µm, Blown Film | 35.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| Yield, 70 µm, Blown Film | 13 | % | |
| Break, 70 µm, Blown Film | 1300 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 18 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 125 | °C | ISO 306/A120 |
| Oxidation Induction Time (200°C) | 120 | min | EN 728 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUNPRENE® FE65HB | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNPRENE® |
| WPP PP PPH2GF3-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Fainplast PVC RKI 715/3 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| HIPLEX® TR-455 natural | HIP-PetroHemija | HDPE | HIPLEX® |
| INNOBATCH® PPH 3260 | Inno-Comp Ltd. | PP Homopolymer | INNOBATCH® |