XENOY™ 5720U resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3GC3G8_XENOY-5720U-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled PBT+PC alloy. Outstanding low temperature impact/chemical resistance. UV stabilized version of XENOY |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Specific Volume | 0.850 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | |||
| 250°C/2.16 kg | 3.8 | g/10 min | ASTM D1238, ISO 1133 |
| 250°C/5.0 kg | 11 | g/10 min | ASTM D1238, ISO 1133 |
| 265°C/2.16 kg | 6.8 | g/10 min | ASTM D1238 |
| 266°C/5.0 kg | 20 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/2.16 kg | 3.60 | cm³/10min | |
| 250°C/5.0 kg | 10.9 | cm³/10min | |
| 265°C/2.16 kg | 6.50 | cm³/10min | |
| 265°C/5.0 kg | 18.9 | cm³/10min | |
| Molding Shrinkage - Flow (3.20 mm) | 1.0 to 1.2 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.28 | % | |
| Equilibrium, 23°C, 50% RH | 0.080 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1830 | MPa | ASTM D638 |
| -- 2 | 1830 | MPa | Internal Method |
| -- 3 | 1820 | MPa | ASTM D638 |
| -- | 1800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 4 | 44.0 | MPa | ASTM D638 |
| Yield 5 | 45.0 | MPa | Internal Method |
| Yield 6 | 47.0 | MPa | ASTM D638 |
| Yield | 44.0 | MPa | ISO 527-2/5 |
| Yield | 47.0 | MPa | ISO 527-2/50 |
| Break 7 | 50.0 | MPa | ASTM D638 |
| Break 8 | 47.0 | MPa | Internal Method |
| Break 9 | 48.0 | MPa | ASTM D638 |
| Break | 43.0 | MPa | ISO 527-2/5, ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 10 | 4.6 | % | ASTM D638 |
| Yield 11 | 4.6 | % | Internal Method |
| Yield 12 | 4.0 | % | ASTM D638 |
| Yield | 4.1 | % | ISO 527-2/5 |
| Yield | 4.6 | % | ISO 527-2/50 |
| Break 13 | 120 | % | ASTM D638 |
| Break 14 | 110 | % | Internal Method |
| Break 15 | 120 | % | ASTM D638 |
| Break | 110 | % | ISO 527-2/5 |
| Break | 120 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 16 | 1660 | MPa | ASTM D790 |
| -- 17 | 1870 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 71.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 18 | 70.0 | MPa | ASTM D790 |
| Break, 50.0 mm Span 19 | 69.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 20 | ISO 179/1eA | ||
| -30°C | 48 | kJ/m² | |
| 23°C | 56 | kJ/m² | |
| Notched Izod Impact | |||
| -40°C | 600 | J/m | ASTM D256 |
| -30°C | 650 | J/m | ASTM D256 |
| -20°C | 700 | J/m | ASTM D256 |
| -10°C | 660 | J/m | ASTM D256 |
| 0°C | 690 | J/m | ASTM D256 |
| 23°C | 720 | J/m | ASTM D256 |
| -40°C 21 | 46 | kJ/m² | ISO 180/1A |
| -30°C 22 | 48 | kJ/m² | ISO 180/1A |
| -20°C 23 | 50 | kJ/m² | ISO 180/1A |
| -10°C 24 | 52 | kJ/m² | ISO 180/1A |
| 0°C 25 | 55 | kJ/m² | ISO 180/1A |
| 23°C 26 | 56 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Energy at Peak Load | 49.5 | J | |
| -40°C, Total Energy | 59.2 | J | |
| -30°C, Energy at Peak Load | 49.5 | J | |
| -30°C, Total Energy | 61.9 | J | |
| -20°C, Energy at Peak Load | 41.9 | J | |
| -20°C, Total Energy | 53.2 | J | |
| 23°C, Energy at Peak Load | 44.8 | J | |
| 23°C, Total Energy | 54.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 108 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 6.40 mm | 117 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 27 | 110 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 83.5 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 95.9 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 28 | 87.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 120 | °C | ASTM D1525, ISO 306/B50 15 29 |
| -- | 122 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 95°C | 9.8E-5 | cm/cm/°C | ASTM E831 |
| Flow : -30 to 80°C | 9.8E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 95°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Transverse : -30 to 80°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 to 80 | % | |
| Rear Temperature | 243 to 266 | °C | |
| Middle Temperature | 249 to 271 | °C | |
| Front Temperature | 254 to 277 | °C | |
| Nozzle Temperature | 254 to 271 | °C | |
| Processing (Melt) Temp | 260 to 277 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.013 to 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 10 mm/min |
| 3 . | 50 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 10 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | Type I, 5.0 mm/min |
| 8 . | Type I, 10 mm/min |
| 9 . | Type I, 50 mm/min |
| 10 . | Type I, 5.0 mm/min |
| 11 . | Type I, 10 mm/min |
| 12 . | Type I, 50 mm/min |
| 13 . | Type I, 5.0 mm/min |
| 14 . | Type I, 10 mm/min |
| 15 . | Type I, 50 mm/min |
| 16 . | 1.3 mm/min |
| 17 . | 2.0 mm/min |
| 18 . | 1.3 mm/min |
| 19 . | 1.3 mm/min |
| 20 . | 80*10*4 sp=62mm |
| 21 . | 80*10*4 |
| 22 . | 80*10*4 |
| 23 . | 80*10*4 |
| 24 . | 80*10*4 |
| 25 . | 80*10*4 |
| 26 . | 80*10*4 |
| 27 . | 80*10*4 mm |
| 28 . | 80*10*4 mm |
| 29 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Gallonprene® GP100-8501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| ELASTOSIL® RT 774 | Wacker Chemie AG | Silicone | ELASTOSIL® RT |
| LAMIGAMID® 710 | Schwartz Technical Plastic | HMWPE | LAMIGAMID® |
| Karina CLEAR PVC COMPONUD -E 794-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pinnacle PP 1112 Z | Pinnacle Polymers | PP Homopolymer | Pinnacle PP |