VENYL SG507 - 8139
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3GB2Ka_VENYL-SG507---8139.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL SG507 - 8139 is a 50 % glass fibre reinforced polyamide 6 intended for Injection moulding. APPLICATIONS VENYL SG507 - 8139 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. VENYL SG500 - 8139 is available in natural but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.57 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.20 to 0.40 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 225 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.6 | % | ISO 527-2 |
| Flexural Modulus | 15200 | MPa | ISO 178 |
| Flexural Stress | 380 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 18 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 98 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+17 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 380 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 245 to 265 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 255 to 275 | °C | |
| Nozzle Temperature | 255 to 275 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| polyvic® M-1838-GL 06 | Unipack Plasindo | PVC, Unspecified | polyvic® |
| Siloxane Masterbatch MB25-504 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| LNP™ THERMOCOMP™ IF008 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOCOMP™ |
| Sylvin 7844-85 Grey 9632 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Neoflex™ 7070 | Zylog Plastalloys Pvt. Ltd. | TPE | Neoflex™ |