Ultramid® B3WGM24 HP
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3G5xWw_Ultramid-B3WGM24-HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass-fibre and mineral reinforced injection moulding grade with outstanding flowability for industrial articles having medium to high rigidity, used e.g. for automobile engine covers, housings, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 90.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 0.59 | -- | % | ISO 294-4 |
| Flow direction | 0.41 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 6.9 - 7.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.1 - 2.5 | -- | % | ISO 62 |
| Viscosity Number (96% H2SO4) | 123 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8500 | 3600 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Yield | -- | 50.0 | MPa | ISO 527-2/50 |
| Fracture | 115 | -- | MPa | ISO 527-2 |
| Tensile Strain | ||||
| Yield | -- | 5.0 | % | ISO 527-2/50 |
| Fracture | 2.7 | -- | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.5 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 8.0 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 45 | 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 8.0 | -- | kJ/m² | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 190 | -- | °C | ISO 75-2/A |
| Melting Temperature | 220 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 80°C | 6.0E-5 - 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 3.4E-5 - 3.8E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1300 | -- | J/kg/°C | |
| Maximum operating temperature- short cycle operation | 180 | -- | °C |
| Additional Information | Dry | Conditioned | ||
|---|---|---|---|---|
| Polymer Abbreviation | PA6-(GF10+M20) | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+10 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.90 | 6.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.20 | IEC 60250 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 270 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Injection instructions |
|---|
| Residence Time : <10 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 3101-10 | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| Xuchuan XCW-6032FB | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| 4LAC® 25H23100 A-M | 4Plas | ABS | 4LAC® |
| Chemlon® 66AR | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Huafon JF-W-3012 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |