POLYshine PBT D221 GF10
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYshine |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3FtXmd_POLYshine-PBT-D221-GF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fibre-reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.3 | % | |
| Flow | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 105 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 5200 | MPa | ISO 178 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 205 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 190 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bayflex® 110-80 (15% Glass) | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| DuraStar™ DS2110UVI | Eastman Chemical Company | Polyester, TP | DuraStar™ |
| Edgetek™ AT-10GF/000 BLACK | PolyOne Corporation | Acetal (POM) Copolymer | Edgetek™ |
| Epoxies, Ect. 20-2370 | Epoxies, Etc. | PUR, Unspecified | Epoxies, Ect. |
| LNP™ LUBRICOMP™ RAL22 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |