AKROMID® B3 GF 45 1 black (3851)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3ESGoK_AKROMID-B3-GF-45-1-black-3851-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength Applications are mainly components in mechanical engineering and in the automotive industry and highly stressed parts in the sports and leisure industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.50 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.30 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 14500 | 8500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 200 | 140 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.5 | 8.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 13000 | 7500 | MPa | ISO 178 |
| Flexural Stress 2 | 315 | 200 | MPa | ISO 178 |
| Flexural Strain at Break 3 | 4.5 | 6.7 | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 45 | -- | % | ISO 1172 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 16 | 15 | kJ/m² | |
| 23°C | 20 | 25 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 95 | 110 | kJ/m² | |
| 23°C | 110 | 110 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 145 | -- | °C | ISO 75-2/C |
| Melting Temperature 4 | 220 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 GB 30 DEL | RTP Company | Acetal (POM) Homopolymer | RTP |
| Styropor® BFL 495 | BASF Corporation | PS (EPS) | Styropor® |
| K-Prene 7000 XL 55 | Technovinyl Polymers India Ltd. | TPV | K-Prene |
| Karina IVORY PVC COMPOUND 40904-35/2-L-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom TRC 787N E G82787 | LyondellBasell Industries | PP Copolymer | Hostacom |