Arnite® T06 204 SN
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Arnite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3DLK4Q_Arnite-T06-204-SN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Arnite® T06 204 SN is a Polybutylene Terephthalate (PBT) material. It is available in Asia Pacific or Europe for injection molding. Important attributes of Arnite® T06 204 SN are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.45 | % | |
| Equilibrium, 23°C, 50% RH | 0.18 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 5.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 165 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 9.0E-5 | cm/cm/°C | |
| Transverse | 9.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.750 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 3.0 to 12 | hr | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 240 | °C | |
| Front Temperature | 240 to 245 | °C | |
| Nozzle Temperature | 240 to 250 | °C | |
| Processing (Melt) Temp | 240 to 250 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell HP671T | LyondellBasell Industries | PP Homopolymer | Purell |
| SURPASS® HPs167-AB | NOVA Chemicals | HDPE | SURPASS® |
| ACRYPET® IR D50 | Mitsubishi Rayon Co., Ltd. | Acrylic (PMMA) | ACRYPET® |
| Lucent PC PC/ABS-1208 | Lucent Polymers, Inc. | PC+ABS | Lucent PC |
| Oleflex™ 6261-70A-8843 Black, 307105 | Vi-Chem Corporation | TPE | Oleflex™ |