EPO-TEK® 377H
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3CheKC_EPO-TEK-377H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EPO-TEK® 377H is a two component, high Tg, graphite filled epoxy designed for ESD/EMI shielding of semiconductor devices and electronics. It can be used in many electronic industries like consumer, military, medical, and optical / OEM / fiber optics. It is an electrically conductive version of EPO-TEK® 377. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 40.0 | µm |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Degradation Temperature | 345 | °C | TGA |
| Die Shear Strength - >10 kg (23°C) | 23.4 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 175 | °C | |
| Intermittent | -55 to 275 | °C | |
| Storage Modulus (23°C) | 2.87 | GPa | |
| Weight Loss on Heating | |||
| 200°C | 0.090 | % | |
| 250°C | 0.66 | % | |
| 300°C | 0.78 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 95.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 5.6E-5 | cm/cm/°C | |
| -- 3 | 2.0E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Transmittance (400 to 1500 nm) | < 0.1 | % |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 1.0 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 4 | Black | ||
| -- 5 | Black | ||
| Density | |||
| Part A | 1.29 | g/cm³ | |
| Part B | 1.33 | g/cm³ | |
| Viscosity 6(23°C) | 0.50 to 1.0 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | 1400 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 80 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa | |
| Volume Resistivity (23°C) | > 4.0E+2 | ohms·cm |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 7995 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Telcar® TL-6085 | Teknor Apex Company | TPE | Telcar® |
| Moplen EP201L | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Karina IVORY PVC COMPOUND 70900-35/ 1-A-AC-LF (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ UX06425 compound | SABIC Innovative Plastics | PPA | LNP™ LUBRICOMP™ |