E-RIALFILL B 02 SD 25 TC
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | E-RIALFILL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3ChSmL_E-RIALFILL-B-02-SD-25-TC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene compound obtained by total recycling of industrial scrap, 25% mineral filler, thermal stabilization for molding process. Good impact strength at ambient temperature, through maintaining thermal properties and stiffness properties of the homopolymer. Specific for profiles extrusion; available just in black color version. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
| Ash Content | 25 | % | ISO 3451 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Oven Aging (150°C) | 5.0 | day | ISO 4577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 73 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 27.0 | MPa | |
| Break, 23°C | 24.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 5.0 | % | |
| Break, 23°C | 200 | % | |
| Flexural Modulus 1(23°C) | 2400 | MPa | ISO 178 |
| Flexural Stress (23°C) | 42.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 2.0 | kJ/m² | |
| -20°C | 2.3 | kJ/m² | |
| 23°C | 4.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 87.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo Epoxy E 3812M-1 | Sumitomo Bakelite North America, Inc. | Epoxy | Sumitomo Epoxy |
| Trademark PE HLP9947 | Trademark Plastics Corporation | HDPE | Trademark PE |
| Ad-Tech Epoxy ES-219 | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| LEXAN™ ML7682 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| KOPPS® S21A65 | Kolon Plastics, Inc. | PPS | KOPPS® |