Epocast 89537-A/B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3CEaNC_Epocast-89537-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DESCRIPTION: Epocast® 89537-A/B epoxy syntactic is a two-part system with glass-fiber reinforcement that can be trowelled or extruded into honeycomb core structures for fastener and attachment potting, core splicing and edge reinforcing. The syntactic has a non-sag consistency that allows for vertical application up to 1/2-inch (1 .25cm) thick. Epocast® 89537-A/B epoxy syntactic is self-extinguishing and meets the requirements of BMS 5-28 Type 7, Class 2. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 0.850 | g/cm³ | ASTM D792 |
| -- 2 | 0.900 | g/cm³ | ASTM D792 |
| -- 3 | 1.00 | g/cm³ | ASTM D792 |
| Viscosity | ASTM D2196 | ||
| -- 4 | Soft-paste | ASTM D2196 | |
| -- 5 | Paste | ASTM D2196 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| flammability- burn rate | mm/min | BMS 5-28 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time - 100 gms (25°C) | 1.2 | hr | ASTM D2471 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time (25°C) | 7.0 | day | |
| Tensile Lap Shear - AL/AL | ASTM D1002 | ||
| -- 6 | 8.27 | MPa | ASTM D1002 |
| -- 7 | 12.4 | MPa | ASTM D1002 |
| -- 8 | 1900 | % | ASTM D1002 |
| Weight Gain 9 | ASTM D543 | ||
| Distilled water | 0.30 | % | ASTM D543 |
| Mil-M-5606, hydraulic fluid | 0.37 | % | ASTM D543 |
| Monsanto Low Density Hydraulic Test Fluid | 0.48 | % | ASTM D543 |
| TT-S-735 Test Fluid | 0.40 | % | ASTM D543 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Modulus | |||
| -- 10 | 3000 | MPa | ASTM D695 |
| -- 11 | 3100 | MPa | ASTM D695 |
| Compressive Strength | ASTM D695 | ||
| -- 12 | 60.7 | MPa | ASTM D695 |
| -- 13 | 59.3 | MPa | ASTM D695 |
| -- 14 | 58.6 | MPa | ASTM D695 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 19 | ||
| Thermoset Mix Viscosity 15(25°C) | 10000 | cP | ASTM D2196 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CURE SCHEDULE:Cure #1 - 7 Days @ 77°FCure # 2 - Gel @ Room Temperature + 90 minutes @ 260°FCure # 3 - Gel @ Room Temperature + 60 minutes @ 350°F |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | System |
| 3 . | Hardener |
| 4 . | System |
| 5 . | Resin |
| 6 . | After Cure #1 |
| 7 . | After Cure #2 |
| 8 . | After Cure #3 |
| 9 . | on immersion - 24 hrs |
| 10 . | After Cure #3 |
| 11 . | After Cure #1 |
| 12 . | After Cure #3 |
| 13 . | After Cure #2 |
| 14 . | After Cure #1 |
| 15 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3960 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Salflex 380A | Salflex Polymers Ltd. | TPV | Salflex |
| RheTech Polypropylene GC10P205-08UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Dynaflex™ G2701-1000-02 | PolyOne Corporation | TPE | Dynaflex™ |
| LUVOCOM® 1850-7315 | Lehmann & Voss & Co. | PBT | LUVOCOM® |