Hostaform® S 9244 XAP² ™ LS
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Hostaform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3BCdhK_Hostaform-S-9244-XAP-LS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POM copolymer, modified Injection molding type, elastomer-containing; with higher impact strength and slightly lower hardness, rigidity and chemical resistance than the basic type HOSTAFORM C 9021 Reduced emission grade, Emission according to VDA 275 < 5 mg/kg good weld strength. Preliminary Datasheet for natural and colored grades |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 1.40 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.6 | % | |
| Flow | 1.7 | % | |
| Water Absorption (Saturation, 23°C) | 1.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1450 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 33.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 7.0 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/1A/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 1200 | MPa | |
| 1000 hr | 650 | MPa | |
| Flexural Modulus (23°C) | 1450 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C, Partial Break | 200 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 68.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 166 | °C | ISO 11357-3 |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.60 | ||
| 1 MHz | 3.60 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 4.0E-3 | ||
| 1 MHz | 6.0E-3 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MELOPAS® MF 152 | RASCHIG GmbH | Mel Formald | MELOPAS® |
| Telene® 1651 | Telene S.A.S., a Rimtec Corporation company | DCPD | Telene® |
| NuSil MED-2000 | NuSil Technology | Silicone | NuSil |
| TECHNYL® A 218HPS V50 BLACK 21N | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® RED |
| Sylvin 8729-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |