HiFill® XRD PA66 0134 LE
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 39pAB8_HiFill-XRD-PA66-0134-LE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon PA66, Metallic Filler, Activated for Metal and X-Ray Detection, Low Extractables for FDA Compliant Applications |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 2.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.0 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 72.4 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 10 | % | ASTM D638 |
| Flexural Modulus | 2830 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 138 | °C | |
| 1.8 MPa, Unannealed | 82.2 | °C | |
| CLTE - Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Nozzle Temperature | 282 to 293 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 54.4 to 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-IM4 | Polymer Resources Ltd. | PC | PRL |
| TRANSMARE® 14CGF20-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| BMC T60-6009 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Hostacom TKC 406P NAT | LyondellBasell Industries | PP, Unspecified | Hostacom |
| ICORENE® N2103 | ICO Polymers EMEA, A Division of A. Schulman | LDPE | ICORENE® |