AMPLIFY™ TY 1451
| Category: | MAH-g , Functional Polymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AMPLIFY™ TY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 38VxSo_AMPLIFY-TY-1451.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AMPLIFY™ TY 1451 Functional Polymer is a maleic anhydride grafted (MAH) polymer. In tie layers for flexible packaging, AMPLIFY TY 1451 Functional Polymer promotes adhesion of Polyethylene to barrier polymers, such as polyamide and ethylene vinyl alcohol (EVOH), and to ionomers and other polar substrates. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.7 | g/10 min | ASTM D1238 |
| MAH Graft Level 1 | Low | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 9.00 | MPa | |
| Break | 8.00 | MPa | |
| Tensile Elongation (Break) | 760 | % | ASTM D638 |
| Flexural Modulus | 186 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Resistance (51 µm) | 8.27 | J/cm³ | Internal Method |
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 51 µm | 225 | MPa | |
| 2% Secant, TD : 51 µm | 269 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 8.96 | MPa | |
| TD : Yield, 51 µm | 10.2 | MPa | |
| MD : Break, 51 µm | 25.5 | MPa | |
| TD : Break, 51 µm | 23.4 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 51 µm | 800 | % | |
| TD : Break, 51 µm | 900 | % | |
| Dart Drop Impact (51 µm) | 140 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 360 | g | |
| TD : 51 µm | 570 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 86.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 122 | °C | Internal Method |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 60 | ASTM D2457 |
| Note Message | |
|---|---|
| 1 . | Low: <0.25 wt%, Medium 0.25-0.5, High >0.5 wt% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Artenius FASTFLOW+ | Artenius | PET | Artenius |
| Crastin® SK692FR BK507 | DuPont Performance Polymers | PBT | Crastin® |
| Daelim Po1y® LL-04S | DAELIM INDUSTRIAL CO., LTD. | LLDPE | Daelim Po1y® |
| KumhoSunny PC/AES HEC0255B | Shanghai KumhoSunny Plastics Co., Ltd. | AES+PC | KumhoSunny PC/AES |
| Karina BLACK PVC COMPOUND 802D48/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |