Latamid 66 S/30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 38AXXp_Latamid-66-S-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 66 (PA66) based compound. Glass beads. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.90 to 1.2 | % | |
| Flow : 2.00 mm | 0.90 to 1.2 | % | |
| Water Absorption (23°C, 24 hr) | 0.27 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 4700 | MPa | |
| 60°C | 2200 | MPa | |
| 90°C | 1200 | MPa | |
| 120°C | 800 | MPa | |
| 150°C | 640 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 60°C | 60.0 | MPa | |
| Yield, 90°C | 40.0 | MPa | |
| Yield, 120°C | 30.0 | MPa | |
| Yield, 150°C | 25.0 | MPa | |
| Break, 23°C | 85.0 | MPa | |
| Break, 60°C | 55.0 | MPa | |
| Break, 90°C | 40.0 | MPa | |
| Break, 120°C | 30.0 | MPa | |
| Break, 150°C | 25.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 60°C | 10 | % | |
| Yield, 90°C | 14 | % | |
| Yield, 120°C | 15 | % | |
| Yield, 150°C | 16 | % | |
| Break, 23°C | 5.0 | % | |
| Break, 60°C | 15 | % | |
| Break, 90°C | 20 | % | |
| Break, 120°C | 25 | % | |
| Break, 150°C | 45 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 0.80 | kJ/m² | |
| 23°C | 1.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 15 | kJ/m² | |
| 23°C | 20 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 235 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 90.0 | °C | |
| Vicat Softening Temperature | 225 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Dimensional Stability | 70.0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 15 | % | |
| Processing (Melt) Temp | 275 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RenPIM® VG 5282 Polyol/ 5281 Isocyanate | Huntsman Advanced Materials | PUR, Unspecified | RenPIM® |
| SHIN-A SER-550 | SHIN-A T&C | Epoxy | SHIN-A |
| Staramide A28 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| CEPLA CT-254 | CEPLA Co., LTD | PP, Unspecified | CEPLA |
| Kepital® F20-52U | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |