APTIV® 1300
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Victrex plc |
| Trademark: | APTIV® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 37zCiE_APTIV-1300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
APTIV® 1300 film is the black version of unfilled semi-crystalline films made from VICTREX® PEEK™ polymer. The film provides a material solution for engineers in ultra-high performance applications offering an alternative option to the APTIV 1000 natural product. APTIV 1300 film has a unique combination of properties providing high temperature performance, light weight, mechanical strength, durability, excellent radiation, hydrolysis and chemical resistance, electrical insulation, wear and abrasion resistance, excellent barrier properties with high purity, good flammability without the use of flame retardants, low toxicity of combustion products and low moisture absorption in a film format. Inherently halogen free and providing ease of processing makes APTIV films a technology enabler for OEMs, our customers and end users. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.30 | g/cm³ | ISO 1183 |
| Shrinkage 1 | |||
| MD : 200°C, 50.0 µm | < 2.0 | % | |
| TD : 200°C, 50.0 µm | < 2.0 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance (23°C, 50.0 µm) | 5.00 | kJ/m² | Internal Method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 50 to 100 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| MD : 23°C, 50 µm | 2500 | MPa | |
| TD : 23°C, 50 µm | 2500 | MPa | |
| MD : 23°C, 100 µm | 2400 | MPa | |
| TD : 23°C, 100 µm | 2300 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 23°C, 50 µm | 120 | MPa | |
| TD : Break, 23°C, 50 µm | 110 | MPa | |
| MD : Break, 23°C, 100 µm | 120 | MPa | |
| TD : Break, 23°C, 100 µm | 110 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 23°C, 50 µm | > 150 | % | |
| TD : Break, 23°C, 50 µm | > 150 | % | |
| MD : Break, 23°C, 100 µm | > 150 | % | |
| TD : Break, 23°C, 100 µm | > 150 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 2(23°C, 0.0500 mm) | 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 3(23°C, 0.0500 mm) | 190 | kV/mm | ASTM D149 |
| Note Message | |
|---|---|
| 1 . | TM-VX-84 |
| 2 . | 100 V |
| 3 . | 6.25 mm electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 D MS | RTP Company | Nylon 612 | RTP |
| Rynite® 935 NC010 | DuPont Performance Polymers | PET | Rynite® |
| Witcom PA6 6G-AS-X | Witcom Engineering Plastics B.V. | Nylon 6 | Witcom PA6 |
| DOW™ HDPE 8262B | The Dow Chemical Company | HDPE | DOW™ HDPE |
| PERCOM® KHT20 | A. Schulman Europe | PP Homopolymer | PERCOM® |