AGILITY™ EC 7100 Performance LDPE
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AGILITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 36LyI3_AGILITY-EC-7100-Performance-LDPE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AGILITY EC 7100 Performance LDPE is an extrusion coating resin designed for thin high speed coatings. This resin can be readily processed using conventional LDPE extrusion coating hardware. For best sensory performance melt temperatures of preferably less than 290°C are chosen. Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.928 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ISO 527-3 | ||
| MD | 10.6 | MPa | |
| TD | 10.4 | MPa | |
| Tensile Elongation 2 | ISO 527-3 | ||
| MD : Break | 360 | % | |
| TD : Break | 400 | % | |
| Seal Initiation Temperature 3 | 97.0 | °C | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| Melting Temperature | 115 | °C | Internal Method |
| Extrusion | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Temperature | 260 to 335 | °C | |
| Draw Down 4(320°C) | 700 | m/min | Internal Method |
| Neck-in 5(320°C) | 176.0 | mm | Internal Method |
| Note Message | |
|---|---|
| 1 . | 25g/m² coating onto Kraft paper substrate or coating web at 250 mm air gap and -15 mm nip off-set.Coatings applied on matte chill roll, surface RT 12 micron. |
| 2 . | 25g/m² coating onto Kraft paper substrate or coating web at 250 mm air gap and -15 mm nip off-set.Coatings applied on matte chill roll, surface RT 12 micron. |
| 3 . | Temperatures at which 3 N/15mm heat seal strength is achieved.25g/m² coating onto Kraft paper substrate or coating web at 250 mm air gap and -15 mm nip off-set.Heat Seal Strength measured at 0.5 sec sealing time, 0.5 N/mm² pressure, 5 mm seal bar.Coatings applied on matte chill roll, surface RT 12 micron. |
| 4 . | Acceleration from 15g/m² at 100 m/min |
| 5 . | 25 g/m² at 100 m/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III HDPE RBF0.08 | ROMPETROL PETROCHEMICALS S.R.L. | HDPE | MIDILENA III |
| Texalan® 6 Series 698A | Austin Novel Materials Co. Ltd. | TPU-Ester/Ether | Texalan® 6 Series |
| BONDYRAM® TL4101B | Polyram Ram-On Industries | PE, Unspecified | BONDYRAM® |
| Hyril® GP355AS | Entec Polymers | SAN | Hyril® |
| Karina CLEAR PVC COMPOUND -E 75/241-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |