Andur 2-92 AP/Curene® 442
| Category: | PUR-Ether/TDI , Polyurethane (Polyether, TDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 35kpPB_Andur-2-92-AP-Curene-442.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur 2-92AP is a polyether (PTMG) based liquid, toluene diisocyanate terminated prepolymer. An elastomer with a hardness of 92 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by reaction with various polyols and their combination with Curene 442 and other diamines, or by the use of plasticizers. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ASTM D1505 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 92 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 5% strain | 1.49 | MPa | ASTM D695 |
| 10% strain | 3.55 | MPa | ASTM D695 |
| 15% strain | 5.65 | MPa | ASTM D695 |
| 25% strain | 8.48 | MPa | ASTM D695 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 10.0 | MPa | ASTM D412 |
| 300% strain | 20.8 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 49.2 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 410 | % | ASTM D412 |
| Compression Set | 27 | % | ASTM D395B |
| Bayshore Resilience | 46 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 5.0 - 6.0 | min | |
| Demold Time | 30 - 40 | min | |
| Post Cure Time (96°C) | 16 | hr |
| Additional Information |
|---|
| Durometer Hardness, ASTM D2240, Shore A: 90 to 94Die C Tear, ASTM D1004: 515 pliAverage Split Tear, ASTM D1938: 110 pliStoichiometry Curative Level: 95%Grams Curene 442 per 100 grams Andur 2 to 92 AP: 13.9 to 16Mix Temperature: Andur 2-92 AP: 180-212°F Curene 442: 230-250°F |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 104 - 121 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vyncolit® X680 | Vyncolit N.V. | Phenolic | Vyncolit® |
| NEFTEKHIM PP 8300G (EPYS30RE) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| ALTECH® PA6 C 2030/219 GF30 IM | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| GERMAMID 6 HV GK 20 HKSZ UV | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |
| KYDEX® XD03 | SEKISUI Polymer Innovations, LLC | PMMA+PVC | KYDEX® |