Devcon Brushable Ceramic Blue/Red

Category:	Epoxy , Epoxy; Epoxide
Manufacturer:	Devcon
Trademark:	Devcon
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	35gg3g_Devcon-Brushable-Ceramic-Blue-Red.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

A brushable, high performance ceramic-filled epoxy for sealing, protecting and repairing surfaces subject to erosion, corrosion and wear.

Intended Use:

Seal and protect new equipment exposed to erosion and corrosion; protect pump casings, impeller blades, gate valves, water boxes, and fan blades; rebuild heat exchangers, tube sheets, and other water circulating equipment; top coat for providing exceptionally smooth surface to repaired surfaces

Product features:

Approved for use in meat and poultry plants (red only)

Excellent chemical resistance

Temperature resistance to 350°F

Applies easily with short-bristle brush or roller

Low viscosity, self-leveling liquid

General Information
Filler / Reinforcement	Ceramic fiber filler
Features	Low viscosity Good chemical resistance
Uses	Repair Materials
Appearance	Red Blue

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.62	g/cm³
Specific Volume	0.618	cm³/g
Solid content- by Volume	100	%

Additional Information	Nominal Value	Unit	Test Method
Salt Spray	6.8	month
Temperature Resistance
Dry	177	°C
Wet	66	°C
Tensile Shear Adhesion	13.8	MPa	ASTM D1002

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage - Flow	0.20	%	ASTM D2566

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	90		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Flexural Strength	55.2	MPa	ASTM D790
Compressive Strength	105	MPa	ASTM D695

Thermal	Nominal Value	Unit	Test Method
CLTE - Flow	3.4E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value		Test Method
Dielectric Constant (1 MHz)	3.87		ASTM D150

Thermoset	Nominal Value	Unit	Test Method
Thermoset Components
Component a	Mixing ratio by weight: 5.6 Mixing ratio by capacity: 3.4
Component B	Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0
Pot Life (24°C)	40	min
Thermoset Mix Viscosity	32000	cP

Additional Information	Nominal Value	Unit	Test Method
Cured 7 days @ 75°F

Uncured Properties	Nominal Value	Unit	Test Method
Curing Time	16	hr

Resin Grade	Manufacturer	Category	Trademark
Riblene® FF 39 D	Versalis S.p.A.	LDPE	Riblene®
Nanjing Hongrui PA66 A333	Nanjing Hongrui Engineering Plastics Co., Ltd.	Nylon 66	Nanjing Hongrui PA66
Fainplast PVC PG 6620	Fainplast Compounds S.r.l	PVC+NBR	Fainplast PVC
LNP™ LUBRICOMP™ DL0029E compound	SABIC Innovative Plastics	PC	LNP™ LUBRICOMP™
Pearlbond™ 539	Lubrizol Advanced Materials, Inc.	TPU-Capro	Pearlbond™