Laticonther 52 CP1/60
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laticonther |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 35Ow4V_Laticonther-52-CP1-60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High thermal conductivity product based on Polypropylene homopolymer (PPh). |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.50 to 1.0 | % | |
| Flow : 2.00 mm | 0.50 to 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 20.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 10 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 115 | °C | ISO 306/B50 |
| Thermal Conductivity | 6.0 | W/m/K | ASTM E1952-01 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3591 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Manner Flexible PVC V937 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SLOVALEN® PQ 91 N | Plastcom | PP, Unspecified | SLOVALEN® |
| Unichem 8818 | Colorite Polymers | PVC, Unspecified | Unichem |
| DURANEX® 7400F | Polyplastics Co., Ltd. | PBT | DURANEX® |