UTTAP SF 50020 GF
| Category: | PESU , Polyethersulfone |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | UTTAP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 349CQt_UTTAP-SF-50020-GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass reinforced (20 %) Polyether Sulfone. Excellent chemical and electrical resistance, high stiffness, modulus and HDT. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 6500 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 125 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.2 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 8200 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 160 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 75 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 205 | °C | ASTM D648 |
| Glass Transition Temperature | 224 | °C | DSC |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tekumid 6 BS | TEKUMA Kunststoff GmbH | Nylon 6 | Tekumid |
| CERTENE™ HI-1752 | Muehlstein | HDPE | CERTENE™ |
| Karina CLEAR PVC COMPOUND 80/211-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SQUARE® LSG6931-20A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |
| Elastoflex® 28100R Resin / 28100T Isocyanate | BASF Corporation | PUR-MDI | Elastoflex® |