Order Products : sales@su-jiao.com
SABIC® HDPE M80064
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 33tRYF_SABIC-HDPE-M80064.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE M80064 is a high density polyethylene injection moulding grade with a narrow molecular weight distribution. It is typically used for injection moulding applications where rigidity, toughness and warp resistance are required. SABIC® HDPE M80064 is available with UV stabilizer as SABIC® HDPE M80064S. Typical applications. SABIC® HDPE M80064 is typically used for the manufacture of injection moulded cases, crates, trays, industrial pails and other similar items. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.964 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 8.0 | g/10 min | |
| 190°C/5.0 kg | 22 | g/10 min | |
| Environmental Stress-Cracking Resistance 1(60°C, 3.00 mm, Rhodacal-DS10, Compression Molded) | 40.0 | hr | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1450 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 32.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 15.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 200 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1700 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 32.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C, Compression Molded) | 4.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 95.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 129 | °C | ISO 306/A |
| Melting Temperature (DSC) | 135 | °C | ISO 11357-3 |
| Enthalpy Change | 229 | J/g | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 to 275 | °C | |
| Mold Temperature | 32.0 to 38.0 | °C | |
| Injection Pressure | 69.0 to 89.0 | MPa |
| Note Message | |
|---|---|
| 1 . | 2 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier LS01018 - A | Premier Polymers, LLC. | LLDPE | Premier |
| Veroplas PA3150 | PlastxWorld Inc. | Nylon 6 | Veroplas |
| DOW鈩?LDPE 219M | The Dow Chemical Company | LDPE | DOW鈩?LDPE |
| Nypol® PA B3 G25 HS PRTA011 NT355 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| LNP™ LUBRICOMP™ RFL36XXY compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |