Witcom PA6 6G-AS-X
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 33srX3_Witcom-PA6-6G-AS-X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Meets ATEX-regulations |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.20 to 0.40 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | < 125 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 to 5.0 | % | ISO 527-2 |
| Flexural Modulus | 6000 | MPa | ISO 178 |
| Flexural Stress | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 16 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 95 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 195 | °C | ISO 75-2/A |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 95.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+9 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | ISO 1210 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TUFNYL® RGF 33 BLACK | SRF Ltd. | Nylon 66 | TUFNYL® |
| Baypreg® 400 | Covestro - PUR | PUR-MDI | Baypreg® |
| Kepital® F30-34 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Hostacom BB 1113 F BLACK | LyondellBasell Industries | PP Copolymer | Hostacom |
| apilon 52® MA-8505 | API SpA | TPU-Polyester | apilon 52® |