Latiblend 7587 E61-V0
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latiblend |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 33kD5E_Latiblend-7587-E61-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polybutylene Terephtalate (PBT)/Polycarbonate (PC). Toughened. UL94 V-0 classified. Very high dimensional stability. Very high impact resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.1 to 1.4 | % | |
| Flow : 2.00 mm | 1.2 to 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 1900 | MPa | |
| 60°C | 1400 | MPa | |
| 90°C | 1200 | MPa | |
| 120°C | 1000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 35.0 | MPa | |
| Yield, 60°C | 25.0 | MPa | |
| Yield, 90°C | 22.0 | MPa | |
| Yield, 120°C | 20.0 | MPa | |
| Break, 23°C | 30.0 | MPa | |
| Break, 60°C | 20.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 5.0 | % | |
| Yield, 60°C | 15 | % | |
| Yield, 90°C | 25 | % | |
| Yield, 120°C | 50 | % | |
| Break, 23°C | 20 | % | |
| Break, 60°C | 75 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact (23°C, 3.20 mm) | No Break | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 130 | °C | |
| Vicat Softening Temperature | 120 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 3.0E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Oxygen Index | 29 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-Comp™ PPBGF40-E | Southland Polymers | PP Impact Copolymer | Pro-Comp™ |
| Xuchuan XCM-18S | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Arnitel® EM740 | DSM Engineering Plastics | TPC-ET | Arnitel® |
| Hanwha Total PP FB51 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| MAXATEL® ACGC15-BK | Pier One Polymers, Inc. | Acetal (POM) Copolymer | MAXATEL® |