NYCOA Polyamide 1417 HS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 32xV4N_NYCOA-Polyamide-1417-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 1417 HS is a heat stabilized and impact modified Nylon 6. This medium viscosity resin was developed for injection molding and extrusion processes for applications requiring improved toughness, flexibility, and good heat stability. NYCOA 1417 HS is suitable for a variety of applications including plugs, connectors, fasteners, clips, tool housings, and flexible tubing extrusion. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.2 | % | |
| Across Flow | 1.4 | % | |
| Water Absorption (24 hr) | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 64.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 75 | % | ASTM D638 |
| Flexural Modulus 3 | 2200 | MPa | ASTM D790 |
| Flexural Strength 4 | 91.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 168 | °C | |
| 1.8 MPa, Unannealed | 66.0 | °C | |
| Melting Temperature | 221 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 221 to 241 | °C | |
| Middle Temperature | 235 to 252 | °C | |
| Front Temperature | 246 to 260 | °C | |
| Nozzle Temperature | 254 to 266 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 76.7 to 87.8 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 to 0.517 | MPa | |
| Cushion | 1.59 to 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Topolymer® 4501 | Dongguan Top Polymer Enterprise | TPEE | Topolymer® |
| Novalloy-A A2601 | PlastxWorld Inc. | ABS+Nylon | Novalloy-A |
| EcoPaXX® Q-KGS6 | DSM Engineering Plastics | Nylon 410 | EcoPaXX® |
| KumhoSunny PC/ABS HAC6020FG | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| Petrothene® GA818073 | LyondellBasell Industries | LLDPE | Petrothene® |