ALTECH® ASA A 1000/720 UV WT1082-11
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALTECH® ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 31vGRh_ALTECH-ASA-A-1000-720-UV-WT1082-11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALTECH® ASA A 1000/720 UV WT1082-11 is an Acrylonitrile Styrene Acrylate (ASA) product. It can be processed by extrusion or injection molding and is available in Asia Pacific, Europe, or North America. Applications of ALTECH® ASA A 1000/720 UV WT1082-11 include automotive and housings. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 5.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 70.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 40.0 | MPa | |
| -- | 40.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 3.0 | % | |
| Break | 14 | % | |
| Flexural Modulus | 2100 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 65.0 | MPa | |
| 3.5% Strain | 60.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -- | 7.0 | kJ/m² | |
| -40°C | 2.0 | kJ/m² | |
| -20°C | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | No Break | ||
| -40°C | 40 | kJ/m² | |
| -20°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 90.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 650 | °C | |
| 2.00 mm | 650 | °C | |
| 3.00 mm | 650 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | |||
| Circulation Dryer | 3.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPUCO® TPU-CH95 | Taiwan PU Corporation | TPU-Polyether | TPUCO® |
| Mylar® MO (500 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Hylex® P1310G40FRMA | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| Pibiflex® E5888 NATURALE | SO.F.TER. SPA | TPC-ET | Pibiflex® |
| LNP™ LUBRICOMP™ SP003 compound | SABIC Innovative Plastics | Nylon 12 | LNP™ LUBRICOMP™ |