DESLEN™ DSC501G4
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESLEN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 31sMdy_DESLEN-DSC501G4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESLEN™ DSC501G4 is Polypropylene Glass Filler 20% reinforced resin. It has good rigidity and Impact resistance. Applications: DESLEN™ DSC501G4 has good mechanical property and rigidity and it is applied to electronic partsand automotive parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 73.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 3920 | MPa | ASTM D790 |
| Flexural Strength | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 150 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 135 | °C | ASTM D648 |
| Melting Temperature | 163 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 190 - 200 | °C | |
| Middle Temperature | 200 - 210 | °C | |
| Front Temperature | 200 - 210 | °C | |
| Nozzle Temperature | 200 - 220 | °C | |
| Processing (Melt) Temp | 200 - 220 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C |
| Injection instructions |
|---|
| Speed: 40 to 70%Pressure 1st: 30 to 60%Pressure 2nd: 30 to 60Holding Pressure: 10 to 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4920 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Premi-Glas® 1266 | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| WellPet® MRGF102R-BK1 | Wellman Engineering Resins | PET | WellPet® |
| Badamid® T70 | Bada AG | Nylon 6/6T | Badamid® |
| Celstran® PP-GF20-02 Black | Celanese Corporation | PP Homopolymer | Celstran® |