EMERGE™ PC/ABS 7590
| Category: | PC+ABS , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 30z8MM_EMERGE-PC-ABS-7590.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC/ABS 7590 advanced resin is an ignition-resistant PC/ABS blend that contains no chlorine or bromine additives. Its superior processing makes it ideal for molding large parts and optimizing cycle time productivity in injection molding operations. It has a UL 94 flammability rating of V-0 a 1.5mm. This resin is suitable for use in a wide variety of applications in the information technology equipment and consumer electronics (ITE/CE) markets. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 230°C/3.8 kg | 17 | g/10 min | |
| 260°C/5.0 kg | 75 | g/10 min | |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 62.1 | MPa | |
| Break, 3.20 mm, Injection Molded | 46.2 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 4.0 | % | |
| Break, 3.20 mm, Injection Molded | 50 | % | |
| Flexural Modulus (3.20 mm, Injection Molded) | 2830 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 97.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 93.9 | °C | |
| 1.8 MPa, Unannealed | 82.2 | °C | |
| Vicat Softening Temperature | 108 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 2(1.50 mm) | V-0 | UL 94 | |
| Oxygen Index 3 | 29 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 to 90.6 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 60.0 to 90.6 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime PE HMWPE 1000 SR | Primex Plastics Corporation | HMWPE | Prime PE |
| Sasol Polymers PP CUV448 | Sasol Polymers | PP Impact Copolymer | Sasol Polymers PP |
| Nylene® BS-700-RA | Custom Resins Group | Nylon 6 | Nylene® |
| TORZEN® G3300L NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| ALCOM® PP 620/40 IM UV BK1021-13MCX | ALBIS PLASTIC GmbH | PP, Unspecified | ALCOM® PP |