MAJORIS CT400
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 30t28n_MAJORIS-CT400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CT400 is a polypropylene 40% mineral filled polypropylene compound intended for injection moulding. The product is available in natural CT400 but other colours can be provided on request. CT400 is intended for components which require good long term heat resistance, it has a high heat distortion temperature, good rigidity, low shrinkage, noice and vibration absorption and good dimensional stability. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.60 - 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 31.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3650 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 131 | °C | ISO 75-2/B |
| CLTE - Flow | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 270 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP564R | LyondellBasell Industries | PP Homopolymer | Moplen |
| TARFLON™ AC1090 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| VICTREX® ST™ P45 | Victrex plc | PEKEKK | VICTREX® ST™ |
| AIE PA66 60G3F | Asia International Enterprise (Hong Kong) Limited | Nylon 66 | AIE PA66 |
| Pinnacle PP 6135C3 | Pinnacle Polymers | PP Random Copolymer | Pinnacle PP |